Fender / checker plate question

[abbeyroad]

It won’t rust. Everything including the rivets are aluminium. Silver rivets will last longer. With black rivets, the colour chips off eventually.

So our front fenders being drilled into are in fact aluminum?

 

[TCMColorado]

Stainless steel rivets with black oxide coating will retain color almost indefinitely. It is not a finish that can flake off. Painted rivets will quickly flake and black anodized aluminum rivets will slowly turn brown from UV exposure unless a UV resistant anodization was used.

 

[TCMColorado]

So our front fenders being drilled into are in fact aluminum?

You can confirm this with the quick application of a magnet.

 

[abbeyroad]

You can confirm this with the quick application of a magnet.

For all I know maybe it's plastic. Just a straight up answer would be appreciated. lmao smh

 

[TCMColorado]

For all I know maybe it's plastic. Just a straight up answer would be appreciated. lmao smh

Using a magnet is not a straight up answer? If a magnet is not attracted to the fender it is either aluminum, stainless steel or another material that will not be subject to corrosion. And the issue at hand is that of corrosion unless I am completely misreading the room.

 

[abbeyroad]

Using a magnet is not a straight up answer? If a magnet is not attracted to the fender it is either aluminum, stainless steel or another material that will not be subject to corrosion. And the issue at hand is that of corrosion unless I am completely misreading the room.

If you dont' want to answer my simple question then don't bother replying dude. lol why so pugnacious?

 

[Krabby]

It’s neither steel nor plastic-it is aluminum (alloy)

 

[TCMColorado]

It’s neither steel nor plastic-it is aluminum (alloy)

Apparently not enough of us can confirm it is aluminum to satisfy the skeptics.

 

[Dogwood]

My concern would by the potential of galvanic corrosion if the fender, rivets, and plates are different metals. If everything is aluminum then you’re probably pretty safe (although it’s still possible if there’s a big enough difference between the aluminum alloys’ galvanic potential). But I would be very cautious about using SS for anything if the fender is aluminum since SS is more noble than aluminum so the aluminum will be the thing that corrodes if the metals are connected electrically to form a galvanic cell (eg are exposed to water + road salt).